2.Cold galvanized steel pipe

Cold galvanized steel pipe

1.“Cold plated” or “plating”, ie the zinc salt solution by electrolysis, to the plating on the coating, generally do not have heating, small amount of zinc, the wet environment is very easy to fall off.

2. Cold galvanizing is the physical address, just brush the surface layer of zinc, the zinc layer is easy to fall off. Construction in the use of hot dip galvanizing.

Cold galvanized zinc is only 10-50g/m2, its own corrosion resistance than hot dip galvanized a lot of difference. Galvanized by a relatively cheaper price.

Hot dip galvanized steel body is hot dip galvanized surface under the condition of its adhesion strong, not easy to fall off, although there hot dip galvanized pipe corrosion phenomenon, but in a very long period to meet technical, health requirements.

3.Cold galvanizing looks more smooth, bright, color passivation process plating layer is yellow-green in color, was colorful. Plating layer was bluish-white or white with white passivation process was green, white coating passivation process and the sun was significant Colorful angle. The complex workpiece angular edges parts prone to “electrical burning” from gloomy, the parts of the zinc layer thick. Yin corner site is easy to form a current dead undercurrent gray area and the area zinc layer is thinner. The workpiece overall zinc tumor, caking phenomenon.

4.Process of cold galvanizing
Cold galvanizing, also called electro-galvanized, is the use of electrolysis device to the workpiece into the composition of the zinc salt solution, after degreasing, pickling, and connecting the negative electrode of the electrolytic device; zinc plate placed at the opposite side of the workpiece is connected in the electrolytic device the positive electrode, the power is turned on, a current from the positive electrode to the negative directional movement, it will be deposited on the workpiece with a layer of zinc.